Polymer Property : Melt Flow = 13.2 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 13.2 - 26.4 g/10 min

@Load 2.16 kg,
Temperature 400 °C
13.2 - 26.4 g/10 min

@Load 4.76 lb,
Temperature 752 °F
ASTM D1183
Gharda Chemicals GATONE™ 5400 PEEK, Medium Viscosity Grade  (discontinued **)
Medium viscosity grade for extrusion and injection moldingCHARACTERISTICS: Outstanding chemical resistance.Outstanding wear resistance.Outstanding resistance to hydrolysis.Excellent mechanical prope..
Melt Flow 13.2 g/10 min

@Load 6.60 kg,
Temperature 337 °C
13.2 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D 1238
SABIC Innovative Plastics Ultem 2212 PEI
20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Melt Flow 13.2 g/10 min

@Load 6.60 kg,
Temperature 337 °C
13.2 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D 1238
SABIC Innovative Plastics Ultem 2212 PEI (Asia Pacific)
20% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region.
Melt Flow 13.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
13.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133
Teijin Panlite® L-1225Y Standard (mold release/ice color grade) Polycarbonate Resin
Injection molding and small-sized injection-blow molding grade that require slightly high fluidity. It has an improved mold release property and is bluish-tinted to exhibit clear color.Applications:..
Melt Flow 13.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
13.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133
Teijin Panlite® L-1225Z100 Transparent and Weather Resistant grade Polycarbonate Resin
Conforms to SAE regulations. It is an injection molding grade that has slightly high fluidity, weather resistance and mold release property and is bluish-tinted to exhibit clear colorApplications:Co..
Melt Flow 13.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
13.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133
Teijin Panlite® LN-1250G Flame Resistant, Translucent Polycarbonate Resin
Flame retardant and mold release grade with normal fluidity, which is suitable for injection molding applications.Applications:Electric, electronic and business machine components that need flame re..
Melt Flow 13.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
13.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133
Teijin Panlite® LN-2250Y Flame Resistant, Translucent Polycarbonate Resin
Flame retardant and mold release grade with normal fluidity, while maintaining intrinsic transparency of polycarbonate resin. It is suitable for injection molding applications.Applications:Electric,..
Melt Flow 13.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
13.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133
Teijin Panlite® LV-2225Y Standard (mold release/ice color grade) Polycarbonate Resin
Flame retardant and mold release grade, while maintaining intrinsic transparency of polycarbonate resin. It is suitable for injection molding applications, required to be slightly high fluidity.Appl..
Melt Flow 13.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
13.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133
Teijin Panlite® LV-2225Z Transparent and Weather Resistant grade Polycarbonate Resin
Injection molding grade that is necessary to be slightly high fluidity. It has weather resistance, mold release property and is bluish-tinted to exhibit clear color.Applications:Components of electr..
Melt Flow 13.2 g/10 min

@Load 2.16 kg,
Temperature 250 °C
13.2 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ISO 1133
BASF Ultradur® B 4406 G6 30% Glass Filled PBT
Description: Is a PBT, flame-retardant injection-molding grades, with 30% glass fibers, for parts requiring enhanced fire resistance, e.g. plug-and-socket connectors, housings, coil formers and ligh..
Melt Flow 13.2 g/10 min

@Load 10.0 kg,
Temperature 250 °C
13.2 g/10 min

@Load 22.0 lb,
Temperature 482 °F
ASTM D1238
SABIC Innovative Plastics NORYL 115 PPE+HIPS (Asia Pacific)
PPE+PS, 115 oC HDT
Melt Flow 13.2 g/10 min

@Load 2.16 kg,
Temperature 250 °C
13.2 g/10 min

@Load 4.76 lb,
Temperature 482 °F
Calculated from Volume Flow Rate of 8 cm<sup>3</sup>/10min.; ISO 1133
DSM Arnite® TV4 260 SF PBT-30% Glass Reinforced (European and Asian Grade)  (discontinued **)
Arnite resins are engineered to provide specific performance in applications where DSM technology can offer value.Arnite Molding resins: Standard Unfilled and Reinforced materialsHigh modulus Flame ..