Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.50 - 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.50 - 1.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polyplastic Armlen® PP GF 20-1EX Polypropylene Copolymer, 20% Glass Fiber Information provided by PolyPlastic Group. |
|||
Melt Flow | 0.80 - 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 - 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Iran Petrochemical (PCC) Arak 1209AA LLDPE
(discontinued **) Information provided by Iran Petrochemical Commercial Co. |
|||
Melt Flow | 0.80 - 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 - 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Iran Petrochemical (PCC) Tabriz 1209AA LLDPE
(discontinued **) Information provided by Iran Petrochemical Commercial Co. |
|||
Melt Flow | 0.40 - 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 - 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Breplast Bretene LD FILM Low Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A. |
|||
Melt Flow | 0.40 - 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.40 - 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
UNI EN ISO 1133 |
Breplast Bretene LD PIPE Low Density Polyethylene Recovered polyethylene compositeInformation provided by Breplast S.p.A. |
|||
Melt Flow | 0.10 - 1.0 g/10 min | 0.10 - 1.0 g/10 min | |
Kazanorgsintez P2ES-12 Electrically Conductive Polyethylene Composite Production Method: P2ES-12 is produced from low density polyethylene, modified by carbon black, rubber and calcium stearate. Application: Designed for production of pipes used for explosive mate.. |
|||
Melt Flow | 0.50 - 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.50 - 1.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polyplastic Armlen® PP GF 30-1EX Polypropylene Copolymer, 30% Glass Fiber Information provided by PolyPlastic Group. |