Polymer Property : Melt Flow = 1.0 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Flow 0.50 - 1.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.50 - 1.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Polyplastic Armlen® PP GF 20-1EX Polypropylene Copolymer, 20% Glass Fiber
Information provided by PolyPlastic Group.
Melt Flow 0.80 - 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 - 1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Iran Petrochemical (PCC) Arak 1209AA LLDPE  (discontinued **)
Information provided by Iran Petrochemical Commercial Co.
Melt Flow 0.80 - 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 - 1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Iran Petrochemical (PCC) Tabriz 1209AA LLDPE  (discontinued **)
Information provided by Iran Petrochemical Commercial Co.
Melt Flow 0.40 - 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.40 - 1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Breplast Bretene LD FILM Low Density Polyethylene
Recovered polyethylene compositeInformation provided by Breplast S.p.A.
Melt Flow 0.40 - 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.40 - 1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
UNI EN ISO 1133
Breplast Bretene LD PIPE Low Density Polyethylene
Recovered polyethylene compositeInformation provided by Breplast S.p.A.
Melt Flow 0.10 - 1.0 g/10 min
0.10 - 1.0 g/10 min
Kazanorgsintez P2ES-12 Electrically Conductive Polyethylene Composite
Production Method: P2ES-12 is produced from low density polyethylene, modified by carbon black, rubber and calcium stearate. Application: Designed for production of pipes used for explosive mate..
Melt Flow 0.50 - 1.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.50 - 1.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Polyplastic Armlen® PP GF 30-1EX Polypropylene Copolymer, 30% Glass Fiber
Information provided by PolyPlastic Group.