Polymer Property : Oxidative Induction Time (OIT) = 30 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Oxidative Induction Time (OIT)	30 min	30 min	At 200°C; ASTM D3895
Borealis Borcell™ HE1105 High Density Polyethylene Compound for Gas Injection of Cellular Coaxial Cables Borcell HE1105 is a high-density polyethylene (HDPE) compound formulated with specific viscosity and melt strength characteristics. Borcell HE1105 is intended for the insulations of coaxial cables ..
Oxidative Induction Time (OIT)	>= 30 min	>= 30 min	EN 728
Total 3802 B HDPE, cable, sheet, pipe, injection molding FINATHENE® 3802 B is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low-pressure slurry polymerization process. FINATHENE® 3802 B is a black polyethylene..
Oxidative Induction Time (OIT)	>= 30 min	>= 30 min	200°C; EN 728
Total 3802 Blue MDPE pipe, injection molding FINATHENE® 3802 Blue is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low pressure slurry polymerization process. FINATHENE® 3802 Blue is a blue polyeth..
Oxidative Induction Time (OIT)	>= 30 min	>= 30 min	200°C; EN 728
Total 3802 YCF MDPE pipe grade FINATHENE® 3802 Y CF is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low pressure slurry polymerization process. FINATHENE® 3802 Y CF is a yellow cadmi..
Oxidative Induction Time (OIT)	>= 30 min	>= 30 min	200°C; EN 728
Total HP 401 MDPE, pipe, cable, sheet FINATHENE® HP 401 is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low-pressure slurry polymerization process. FINATHENE® HP 401 is a black high densit..
Oxidative Induction Time (OIT)	>= 30 min	>= 30 min	200°C; EN 728
Total LF 38 YS CF MDPE, pipe FINATHENE® LF 38 YS CF is a cadmium-free yellow stripe compound designed to be used in combination with FINATHENE® 3802 B for gas pipe application. The base polymer of FINATHENE® LF 38 YS CF is t..
Oxidative Induction Time (OIT)	>= 30 min @Temperature 190 °C	>= 30 min @Temperature 374 °F	ISO 11357-6
Addcomp PRIEX® 25093 Maleic Anhydride Grafted PP random copolymer Functionalised polypropylene to be used as compatibiliser for polymer blends or coupling agent for glass fibre, wood flour, natural fibres, multilayer films, aluminium foils, or mineral filled polyp..
Oxidative Induction Time (OIT)	>= 30 min	>= 30 min	200°C; EN 728
Total Lacqtene® 2001 TBK 46 HDPE pipe (discontinued **) LACQTENE® 2001 TBK 46 is a high density polyethylene produced by the gas phase polymerization process. LACQTENE® 2001 TBK 46 is a black compound especially developed for pressure pipe for gas and ..