Physical Properties | Metric | English | Comments |
---|---|---|---|
Oxidative Induction Time (OIT) | >= 20 min @Temperature 210 °C |
>= 20 min @Temperature 410 °F |
EN 728 |
SABIC P5510 Black High Density Polyethylene for Pipes Product Description: P5510 is a black compound high density (class MRS 8 - PE 80) polyethylene with bimodal distribution of molecular mass. It is specifically designed for Pressure Pipe applicatio.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2001 PBK 44 HDPE pipe
(discontinued **) LACQTENE® 2001 PBK 44 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2001 PBK 44 is a black compound especially developed for s.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2001 TYL 46 HDPE pipe
(discontinued **) LACQTENE® 2001 TYL 46 is a cadmium-free yellow stripe compound designed to be used in combination with LACQTENE® 2001 TBK 46 for gas pipe application. The base polymer of LACQTENE® 2001 TYL 46 is.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2002 TBL 40 HDPE pipe
(discontinued **) LACQTENE® 2002 TBL 40 is a blue stripe compound designed to be used in combination with LACQTENE® 2002 TBK 40 for gas pipe application. The base polymer of LACQTENE® 2002 TBL 40 is the same as th.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2002 TYL 40 HDPE pipe
(discontinued **) LACQTENE® 2002 TYL 40 is a cadmium-free yellow stripe compound designed to be used in combination with LACQTENE® 2002 TBK 40 for gas pipe application. The base polymer of LACQTENE® 2002 TYL 40 is.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2006 PBK 35 HDPE pipe, sheet
(discontinued **) LACQTENE® 2006 PBK 35 is a medium density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2006 PBK 35 may be used for pipe extrusion (micro-irriga.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2006 TN 35 HDPE pipe coating
(discontinued **) LACQTENE® 2006 TN 35 is a medium density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2006 TN 35 may be used for pipe and sheet extrusion (flex.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | ASTM D3895 modified (excludes copper mesh), 200°C |
Ineos TC46-25 HDPE TC46-25 is a natural high density polyethylene copolymer designed specifically for telecommunications ducting to meet or exceed the material requirements in ASTM F2160, UL 651B and MEMA TC-7. TC46-.. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 210 °C |
>= 20 min @Temperature 410 °F |
ASTM D3895 |
Ineos TUB 121NTW HDPE TUB121 NTW is a natural high density bimodal polyethylene copolymer designed for extrusion of large diameter, thick wall piping for potable water, industrial and mining applications. When blended wi.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | ASTM D3895 |
Ineos TUB 172 HDPE TUB 172 is a yellow medium density polyethylene copolymer designed specifically for the extrusion of natural gas pipe. It exhibits excellent long term stress life and slow crack growth resistance. T.. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 210 °C |
>= 20 min @Temperature 410 °F |
ASTM D3895 |
Ineos K44-06-122 HDPE HDPE K44-06-122 is a natural high density polyethylene copolymer designed specifically for extrusion of potable water, industrial, and mining pipe. It is recognized by the Plastic Pipe Institute as .. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 200 °C |
>= 20 min @Temperature 392 °F |
ISO/TR10837 |
SCG Chemicals EL-Leneâ„¢ H5211PBL High Density Polyethylene Pipe Resin Key Characteristics: Good processing, high thermal stability, good resistance to weatheringRecommended Applications: Stripe lines for PE80 pipe, non pressure pipesCertification: Certified by LNEI.. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 200 °C |
>= 20 min @Temperature 392 °F |
ISO/TR10837 |
SCG Chemicals EL-Leneâ„¢ H570P High Density Polyethylene Pipe Resin Key Characteristics: High stiffness, good processingRecommended Applications: Corrugated pipes, non pressure pipes, conduit, sewage drainage pipesInformation provided by SCG Chemicals |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total 3802 Blue MDPE pipe, injection molding FINATHENE® 3802 Blue is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low pressure slurry polymerization process. FINATHENE® 3802 Blue is a blue polyeth.. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 200 °C |
>= 20 min @Temperature 392 °F |
EN 728 |
Borealis BorSafe™ HE3490-IM HDPE Compound for Injection Molded Pressure Fittings BorSafe™ HE3490-IM is a bimodal polyethylene compound produced by the advanced Borstar® technology. Well dispersed carbon black gives outstanding UV resistance. Long term stability is ensured by .. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total 3802 YCF MDPE pipe grade FINATHENE® 3802 Y CF is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low pressure slurry polymerization process. FINATHENE® 3802 Y CF is a yellow cadmi.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total HP 401 MDPE, pipe, cable, sheet FINATHENE® HP 401 is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low-pressure slurry polymerization process. FINATHENE® HP 401 is a black high densit.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Xsene® XS10 B HDPE, pipe, injection molding FINATHENE® XS10 B is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS10 B is a high performance black compound speci.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Xsene® XS10 BRS HDPE, pipe FINATHENE® XS 10 BRS is a brown stripe compound designed to be used in combination with the black PE 100 grade FINATHENE® XS 10 B for sewage application. The base polymer of FINATHENE® XS 10 BRS .. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Xsene® XS10 H HDPE, pipe, injection molding FINATHENE® XS 10 H is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS 10 H is a high performance dark blue compound.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total Xsene® XS10 H HDPE, pipe, injection molding FINATHENE® XS 10 H is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS 10 H is a high performance dark blue compound.. |
|||
Oxidative Induction Time (OIT) | 20 min @Temperature 210 °C |
20 min @Temperature 410 °F |
ISO 11357-6 |
Addcomp PRIEX® 12031 Maleic Anhydride Grafted HDPE Fields of application: Functionalised polyethylene to be used as compatibiliser for polymer blends or coupling agent for wood flour, natural fibres, or mineral filled polyolefins. Also suitable to r.. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 210 °C |
>= 20 min @Temperature 410 °F |
ISO 11357-6 |
Addcomp PRIEX® 15005 Maleic Anhydride modified LDPE Functionalised low density polyethylene to be used as compatibiliser for polymer blends or coupling agent for wood flour, natural fibres, or mineral filled polyolefins. Also suitable to reduce pigme.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2002 TN 40 HDPE, blow molding, pipe, sheet
(discontinued **) LACQTENE® 2002 TN 40 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer.Information provided provided by Total Petrochemicals.Total Petrochemic.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total Lacqtene® 2001 TBK 46 HDPE pipe
(discontinued **) LACQTENE® 2001 TBK 46 is a high density polyethylene produced by the gas phase polymerization process. LACQTENE® 2001 TBK 46 is a black compound especially developed for pressure pipe for gas and .. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2001 TN 46 HDPE pipe
(discontinued **) LACQTENE® 2001 TN 46 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2001 TN 46 is used for sewage pipe, smooth protective condu.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Xsene® XS10 Orange YCF HDPE, pipe FINATHENE® XS 10 ORANGE YCF is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS 10 ORANGE YCF is a high performance .. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total Xsene® XS10 Orange YCF HDPE, pipe FINATHENE® XS 10 ORANGE YCF is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS 10 ORANGE YCF is a high performance .. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 200 °C |
>= 20 min @Temperature 392 °F |
ISO/TR10837 |
SCG Chemicals EL-Lene™ H5211PYL High Density Polyethylene Pipe Resin Key Characteristics: Good processing, high thermal stability, good resistance to weatheringRecommended Applications: Stripe lines for PE80 pipe, non pressure pipesCertification: Certified by LNEI.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Xsene® XS10 YS HDPE, pipe FINATHENE® XS 10 YS is a cadmium-free yellow stripe compound designed to be used in combination with the black PE 100 grade FINATHENE® XS 10 B for gas pipe application. The base polymer of FINATHE.. |