Physical Properties | Metric | English | Comments |
---|---|---|---|
Oxidative Induction Time (OIT) | >= 20 min @Temperature 210 °C |
>= 20 min @Temperature 410 °F |
EN 728 |
SABIC P6006 Black High Density Polyethylene for Pipes Product Description: P6006 is a black compound high density (class MRS 8 - PE 80) polyethylene with bimodal distribution of molecular mass. It is specifically designed for Pressure Pipe applicatio.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2001 PBK 44 HDPE pipe
(discontinued **) LACQTENE® 2001 PBK 44 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2001 PBK 44 is a black compound especially developed for s.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2001 TMA 46 HDPE pipe
(discontinued **) LACQTENE® 2001 TMA 46 is a brown stripe compound designed to be used in combination with LACQTENE® 2001 TBK 46 for gas pipe application. The base polymer of LACQTENE® 2001 TMA 46 is the same as t.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2001 TYL 46 HDPE pipe
(discontinued **) LACQTENE® 2001 TYL 46 is a cadmium-free yellow stripe compound designed to be used in combination with LACQTENE® 2001 TBK 46 for gas pipe application. The base polymer of LACQTENE® 2001 TYL 46 is.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2002 TBL 40 HDPE pipe
(discontinued **) LACQTENE® 2002 TBL 40 is a blue stripe compound designed to be used in combination with LACQTENE® 2002 TBK 40 for gas pipe application. The base polymer of LACQTENE® 2002 TBL 40 is the same as th.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2002 TYL 40 HDPE pipe
(discontinued **) LACQTENE® 2002 TYL 40 is a cadmium-free yellow stripe compound designed to be used in combination with LACQTENE® 2002 TBK 40 for gas pipe application. The base polymer of LACQTENE® 2002 TYL 40 is.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2006 PBK 35 HDPE pipe, sheet
(discontinued **) LACQTENE® 2006 PBK 35 is a medium density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2006 PBK 35 may be used for pipe extrusion (micro-irriga.. |
|||
Oxidative Induction Time (OIT) | 20 min | 20 min | @210 C > 20 Min; ASTM D 3895 |
Ineos K38-20-160 Polyethylene Copolymer K38-20-160 is a medium density polyethylene copolymer containing an organic yellow pigment system, designed specifically for the extrusion of natural gas pipe. It exhibits excellent long term stres.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | ASTM D3895 modified (excludes copper mesh), 200°C |
Ineos TC46-25 HDPE TC46-25 is a natural high density polyethylene copolymer designed specifically for telecommunications ducting to meet or exceed the material requirements in ASTM F2160, UL 651B and MEMA TC-7. TC46-.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | ASTM D3895 |
Ineos TUB 172 HDPE TUB 172 is a yellow medium density polyethylene copolymer designed specifically for the extrusion of natural gas pipe. It exhibits excellent long term stress life and slow crack growth resistance. T.. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 200 °C |
>= 20 min @Temperature 392 °F |
EN 728 |
Borealis BorSafe™ HE3494-LS-H HDPE Compound for Pressure Pipes BorSafe™ HE3494-LS-H is a bimodal polyethylene compound produced by the advanced Borstar® technology. It includes a combination of pigments and stabilizers to ensure excellent long-term thermal s.. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 200 °C |
>= 20 min @Temperature 392 °F |
EN 728 |
Borealis BorSafe™ ME3420 MDPE Compound for Pressure Pipes BorSafe™ ME3420 is a bimodal polyethylene compound produced by the advanced Borstar® technology. Well dispersed carbon black gives outstanding UV resistance. Long term stability is ensured by an .. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total 3802 Blue MDPE pipe, injection molding FINATHENE® 3802 Blue is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low pressure slurry polymerization process. FINATHENE® 3802 Blue is a blue polyeth.. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 210 °C |
>= 20 min @Temperature 410 °F |
EN 728 |
Borealis BorSafe™ HE3490-LS-H HDPE Compound for Pressure Pipes BorSafe™ HE3490-LS-H is a bimodal polyethylene compound produced by the advanced Borstar® technology. It includes a combination of pigments and stabilizers to ensure excellent long-term thermal s.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total 3802 YCF MDPE pipe grade FINATHENE® 3802 Y CF is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low pressure slurry polymerization process. FINATHENE® 3802 Y CF is a yellow cadmi.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total HP 401 MDPE, pipe, cable, sheet FINATHENE® HP 401 is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low-pressure slurry polymerization process. FINATHENE® HP 401 is a black high densit.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Xsene® XS10 B HDPE, pipe, injection molding FINATHENE® XS10 B is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS10 B is a high performance black compound speci.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total Xsene® XS10 B HDPE, pipe, injection molding FINATHENE® XS10 B is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS10 B is a high performance black compound speci.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Xsene® XS10 BRS HDPE, pipe FINATHENE® XS 10 BRS is a brown stripe compound designed to be used in combination with the black PE 100 grade FINATHENE® XS 10 B for sewage application. The base polymer of FINATHENE® XS 10 BRS .. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Xsene® XS10 H HDPE, pipe, injection molding FINATHENE® XS 10 H is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS 10 H is a high performance dark blue compound.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total Xsene® XS10 H HDPE, pipe, injection molding FINATHENE® XS 10 H is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS 10 H is a high performance dark blue compound.. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 210 °C |
>= 20 min @Temperature 410 °F |
ISO 11357-6 |
Addcomp PRIEX® 15005 Maleic Anhydride modified LDPE Functionalised low density polyethylene to be used as compatibiliser for polymer blends or coupling agent for wood flour, natural fibres, or mineral filled polyolefins. Also suitable to reduce pigme.. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 190 °C |
>= 20 min @Temperature 374 °F |
ISO 11357-6 |
Addcomp PRIEX® 20093 Maleic Anhydride Grafted PP homopolymer Functionalised polypropylene to be used as compatibiliser for polymer blends or coupling agent for glass fiber, wood flour, natural fibers, multilayer films, aluminum foils, or mineral filled polypr.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total Lacqtene® 2001 TBK 46 HDPE pipe
(discontinued **) LACQTENE® 2001 TBK 46 is a high density polyethylene produced by the gas phase polymerization process. LACQTENE® 2001 TBK 46 is a black compound especially developed for pressure pipe for gas and .. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2001 TBK 40 HDPE pipe
(discontinued **) LACQTENE® 2002 TBK 40 is a medium density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2002 TBK 40 is a black compound especially developed for.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Xsene® XS10 Orange YCF HDPE, pipe FINATHENE® XS 10 ORANGE YCF is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS 10 ORANGE YCF is a high performance .. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 210°C; EN 728 |
Total Xsene® XS10 Orange YCF HDPE, pipe FINATHENE® XS 10 ORANGE YCF is a high density polyethylene based on C6 hexene as co-monomer and is produced by the Fina Double Loop Technology™. FINATHENE® XS 10 ORANGE YCF is a high performance .. |
|||
Oxidative Induction Time (OIT) | >= 20 min @Temperature 200 °C |
>= 20 min @Temperature 392 °F |
ISO/TR10837 |
SCG Chemicals EL-Lene™ H5211PYL High Density Polyethylene Pipe Resin Key Characteristics: Good processing, high thermal stability, good resistance to weatheringRecommended Applications: Stripe lines for PE80 pipe, non pressure pipesCertification: Certified by LNEI.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | 200°C; EN 728 |
Total Lacqtene® 2001 TBL 46 HDPE pipe
(discontinued **) LACQTENE® 2001 TBL 46 is a blue stripe compound designed to be used in combination with LACQTENE® 2001 TBK 46 for gas pipe application. The base polymer of LACQTENE® 2001 TBL 46 is the same as th.. |
|||
Oxidative Induction Time (OIT) | >= 20 min | >= 20 min | ASTM D3895 |
Reliance Industries Relene B31101 Polyethylene Steel pipe coating base High Density Polyethylene resin. Characteristics:broad molecular weight distribution, good melting strength, excellent toughness/ESCR, and good cut through/abrasion resistanc.. |