Polymer Property : Melt Index of Compound = 7.0 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Index of Compound	2.0 - 7.0 g/10 min	2.0 - 7.0 g/10 min
Sibur L-85M Polyvinyl Chloride (PVC) For use in the footwear industry for production of shoe soles.
Melt Index of Compound	6.0 - 7.0 g/10 min	6.0 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Melt Index of Compound	6.0 - 7.0 g/10 min	6.0 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Melt Index of Compound	5.5 - 7.0 g/10 min	5.5 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Melt Index of Compound	6.0 - 7.0 g/10 min	6.0 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Melt Index of Compound	5.5 - 7.0 g/10 min	5.5 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Melt Index of Compound	5.5 - 7.0 g/10 min	5.5 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Melt Index of Compound	6.0 - 7.0 g/10 min	6.0 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Melt Index of Compound	5.5 - 7.0 g/10 min	5.5 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Melt Index of Compound	6.0 - 7.0 g/10 min	6.0 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Melt Index of Compound	6.0 - 7.0 g/10 min	6.0 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from ..
Melt Index of Compound	5.5 - 7.0 g/10 min	5.5 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Melt Index of Compound	5.5 - 7.0 g/10 min	5.5 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..