Polymer Property : Melt Index of Compound = 65 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Index of Compound	65 g/10 min @Load 10.0 kg, Temperature 190 Â°C	65 g/10 min @Load 22.0 lb, Temperature 374 Â°F	cm<sup>3</sup>/10 min
Huntsman IROGRANÂ® A 85 E 4993 FCM Polyester-Based TPU-Injection Extrusion Grade IROGRAN A 85 E 4993 FCM is a thermoplastic polyester polyurethane for melt calendaring. IROGRAN is part of the HUNTSMAN technical extrusion and injection molding product range and offers a specially..
Melt Index of Compound	65 g/10 min @Load 21.6 kg, Temperature 190 Â°C	65 g/10 min @Load 47.6 lb, Temperature 374 Â°F	cm<sup>3</sup>/10 min
Huntsman IROGRANÂ® A 85 P 4441 TPU-Polyether Introduction: IROGRAN A 85 P 4441 is a polyether based thermoplastic polyurethane intended for injection molding and extrusion applications. IROGRAN A 85 P 4441 is part of the HUNTSMAN technical ext..
Melt Index of Compound	65 g/10 min @Load 21.6 kg, Temperature 190 Â°C	65 g/10 min @Load 47.6 lb, Temperature 374 Â°F	MVR, [cm<sup>3</sup>/10 min]
Huntsman IROGRANÂ® A 87 P 4946 TPU-Polyester Introduction: IROGRAN A 87 P 4946 is a polyether based thermoplastic polyurethane intended for injection molding and extrusion applications. IROGRAN A 87 P 4946 is part of the HUNTSMAN technical ext..
Melt Index of Compound	65 g/10 min @Load 5.00 kg, Temperature 360 Â°C	65 g/10 min @Load 11.0 lb, Temperature 680 Â°F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics ULTEM 9085 PEI Blend High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution.
Melt Index of Compound	65 g/10 min @Load 5.00 kg, Temperature 360 Â°C	65 g/10 min @Load 11.0 lb, Temperature 680 Â°F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Asia Pacific) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution.
Melt Index of Compound	65 g/10 min @Load 5.00 kg, Temperature 360 Â°C	65 g/10 min @Load 11.0 lb, Temperature 680 Â°F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Europe-Africa-Middle East) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 55/55 with low toxicity, smoke and flame evolution.