Polymer Property : Melt Index of Compound = 5.5 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Index of Compound	5.5 g/10 min @Load 3.80 kg, Temperature 190 °C	5.5 g/10 min @Load 8.38 lb, Temperature 374 °F	ASTM D1238
Ovation Polymers SOFTAPLAS™ S 56A Thermoplastic Elastomer Thermoplastic Elastomer – Excellent hydrolytic Stability and balance of properties. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are p..
Melt Index of Compound	5.5 g/10 min @Load 2.16 kg, Temperature 325 °C	5.5 g/10 min @Load 4.76 lb, Temperature 617 °F	DAM; cm3/10 min; ISO 1133
DuPont Performance Polymers Zytel® HTN 54G35HSLR NC010 Polyphthalamide (PPA) (Unverified Data**) Zytel® HTN54G35HSLR NC010 is a 35% glass reinforced, toughened, heat stabilized, lubricated high performance polyamide resin. It is also a PPA resin.Information provided by DuPont Performance Polym..
Melt Index of Compound	5.5 g/10 min @Load 3.80 kg, Temperature 230 Â°C	5.5 g/10 min @Load 8.38 lb, Temperature 446 Â°F	ASTM D1238
LG Chemical HI855S PMMA, Impact Resistant Grade Molding granule designed for greater impact strength combined with the outstanding properties of conventional acrylic materialsFeatures: Excellent transparency and eleganceWeather resistance and che..
Melt Index of Compound	5.5 - 7.0 g/10 min	5.5 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Melt Index of Compound	5.5 - 7.0 g/10 min	5.5 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Melt Index of Compound	5.5 - 7.0 g/10 min	5.5 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Melt Index of Compound	5.5 - 7.0 g/10 min	5.5 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Melt Index of Compound	5.5 - 7.0 g/10 min	5.5 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..
Melt Index of Compound	5.5 g/10 min @Load 5.00 kg, Temperature 280 °C	5.5 g/10 min @Load 11.0 lb, Temperature 536 °F	cm3/10 min; ISO 1133
DuPont Performance Polymers Rynite® 408 NC010 PET Rynite® 408 NC010 is a 30% glass reinforced modified polyethylene terephthalate with improved impact resistance. Excellent balance of strength, stiffness, toughness, and temperature resistance.Inf..
Melt Index of Compound	5.5 g/10 min @Load 21.6 kg, Temperature 150 °C	5.5 g/10 min @Load 47.6 lb, Temperature 302 °F	Fainplast
Fainplast Compounds HAX HF 4121 Halogen Free PVC General purpose
Melt Index of Compound	5.5 - 9.3 g/10 min @Load 2.16 kg, Temperature 190 °C	5.5 - 9.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Arkema Group OREVAC® 9304 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre..
Melt Index of Compound	5.5 - 7.0 g/10 min	5.5 - 7.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa..