Polymer Property : Melt Index of Compound = 37 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Index of Compound	37 g/10 min @Load 10.0 kg, Temperature 220 °C	37 g/10 min @Load 22.0 lb, Temperature 428 °F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Cycolac® FR23 ABS Flame retardant ABS (non-PBBE additives). Good properties/toughness. Excellent moldability. UL94 V-0 rated.
Melt Index of Compound	37 g/10 min @Load 10.0 kg, Temperature 220 °C	37 g/10 min @Load 22.0 lb, Temperature 428 °F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Cycolac® FR23 ABS (Asia Pacific) Flame retardant ABS (non-PBBE additives). Good properties/toughness. Excellent moldability. UL94 V-0 rated.
Melt Index of Compound	37 g/10 min @Load 5.00 kg, Temperature 300 Â°C	37 g/10 min @Load 11.0 lb, Temperature 572 Â°F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics LNP THERMOCOMP DX10311 PC (Asia Pacific) DX10311 is 30% glass fiber reinforced, impact modified polycarbonate resin. High flow and good ductility.
Melt Index of Compound	37 g/10 min @Load 2.16 kg, Temperature 230 °C	37 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Arkema Group OREVAC® 18751 Maleic Anhydride Modified Polypropylene DescriptionOREVAC 18751 is a coextrusion coating adhesive based on a maleic anhydride modified polypropylene resin. It combines the processability of an extrusion coating resin with the thermal resi..
Melt Index of Compound	37 g/10 min @Load 5.00 kg, Temperature 280 °C	37 g/10 min @Load 11.0 lb, Temperature 536 °F	MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics NORYL PX1005X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/5VA rated. UL746C F1. Excelent dielectric strength. Suitable for E/E market in indoor/outdoor applications.