Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Index of Compound | 35 g/10 min @Load 5.00 kg, Temperature 260 °C |
35 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
Polykemi AB POLYblend 83FR PC/ABS-Blend, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
Melt Index of Compound | 35 g/10 min @Load 5.00 kg, Temperature 260 °C |
35 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
Polykemi AB POLYblend 85 M10 PC/ABS-Blend Information provided by Polykemi AB |
|||
Melt Index of Compound | 35 g/10 min @Load 5.00 kg, Temperature 260 °C |
35 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
Polykemi AB SCANBLEND FS7 FR UV PC/ASA Blend, Flame-Retardant, UV Stabilized Information provided by Polykemi AB |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Polykemi AB SCANFILL Injection CPC35051 PP/PE, Mineral Reinforced Information provided by Polykemi AB |
|||
Melt Index of Compound | 35 g/10 min @Load 21.6 kg, Temperature 190 °C |
35 g/10 min @Load 47.6 lb, Temperature 374 °F |
MVR, [cm<sup>3</sup>/10 min] |
Huntsman IROGRAN® A 85 E 4607 E TPU-Polyester Introduction: IROGRAN A 85 E 4607 is a thermoplastic polyether- polyurethane intended for extrusion and injection molding applications. Additional characteristics of the product are excellent mechan.. |
|||
Melt Index of Compound | 35 g/10 min @Load 8.70 kg, Temperature 160 °C |
35 g/10 min @Load 19.2 lb, Temperature 320 °F |
MVR |
Huntsman IROGRAN® A 60 E 4902 TPU-Polyester Introduction: IROGRAN A 60 E 4902 is a soft, high performance polyester based thermoplastic polyurethane intended for extrusion and molding applications. IROGRAN A 60 E 4902 is part of the HUNTSMAN .. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 265 °C |
35 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® IQ8280SF PBT+PET Valox iQ8280SF resin is an environmentally responsible, low carbon footprint, and sustainable resin. Valox iQ8280SF resin offer Super High Flow characteristics combined with high modulus and excell.. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 265 °C |
35 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® IQ8280SF PBT+PET (Asia Pacific) Valox iQ8280SF resin is an environmentally responsible, low carbon footprint, and sustainable resin. Valox iQ8280SF resin offer Super High Flow characteristics combined with high modulus and excell.. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 265 °C |
35 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics Valox® IQ8280SF PBT+PET (Europe-Africa-Middle East) Valox iQ8280SF resin is an environmentally responsible, low carbon footprint, and sustainable resin. Valox iQ8280SF resin offer Super High Flow characteristics combined with high modulus and excell.. |
|||
Melt Index of Compound | 35 g/10 min @Load 1.20 kg, Temperature 300 °C |
35 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics LNP THERMOCOMP Lexan_BFL2200 PC (Asia Pacific) design for black light frame application as high flow PC, V-2, high reflection grade. |
|||
Melt Index of Compound | 35 g/10 min @Load 1.20 kg, Temperature 300 °C |
35 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
SABIC Innovative Plastics LNP THERMOCOMP Lexan_BFL2200 PC (Europe-Africa-Middle East) design for black light frame application as high flow PC, V-2, high reflection grade. |
|||
Melt Index of Compound | 35 g/10 min | 35 g/10 min | 2.16/190; ASTM D1238 |
A. Schulman SCHULAFLEX® SF 230 Ethylene-Based Butene Plastomer DescriptionSchulaflex SF230 is an ethylene-based butene plastomer. Available in natural as a non-UV stable product. It can be compounded as natural or colors with a full UV package.NOTE: Physical .. |
|||
Melt Index of Compound | 35 g/10 min | 35 g/10 min | 2.16/190; ASTM D1238 |
A. Schulman SCHULAFLEX® SF 230 Ethylene-Based Butene Plastomer DescriptionSchulaflex SF230 is an ethylene-based butene plastomer. Available in natural as a non-UV stable product. It can be compounded as natural or colors with a full UV package.NOTE: Physical .. |
|||
Melt Index of Compound | 35 g/10 min | 35 g/10 min | 2.16/190; ASTM D1238 |
A. Schulman SCHULAFLEX® SF 230 Ethylene-Based Butene Plastomer DescriptionSchulaflex SF230 is an ethylene-based butene plastomer. Available in natural as a non-UV stable product. It can be compounded as natural or colors with a full UV package.NOTE: Physical .. |
|||
Melt Index of Compound | 35 g/10 min | 35 g/10 min | 2.16/190; ASTM D1238 |
A. Schulman SCHULAFLEX® SF 230 Ethylene-Based Butene Plastomer DescriptionSchulaflex SF230 is an ethylene-based butene plastomer. Available in natural as a non-UV stable product. It can be compounded as natural or colors with a full UV package.NOTE: Physical .. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Dow 5E16S Polypropylene Homopolymer Resin OverviewConsistent processabilitySuperior impactGood mold releaseContains an antistatic additiveComplies with U.S. FDA 21 CFR 177.1520 (c)1.1aComplies with Canadian HPFB No ObjectionDOW 5E16S Polypr.. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Dow 6D43 Polypropylene Random Copolymer Resin OverviewConsistent processabilityGood spinning characteristicsComplies with U.S. FDA 21 CFR 177.1520 (c)3.1aDOW 6D43 Polypropylene Resin is intended for use in fiber spinning processes.Dow Announced.. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Dow C700-35 Polypropylene Impact Copolymer Resin OverviewHigh stiffnessGood mold fillabilityComplies with: U.S. FDA FCN 843, Canadian HPFB No ObjectionDOW C700-35 Polypropylene Resin is intended for use in injection molding processes where medium .. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Dow C700-35N Polypropylene Impact Copolymer Resin OverviewGood mold fillabilityHigh stiffnessFast set-upContains a nucleating additiveComplies with: U.S. FDA FCN 843, Canadian HPFB No ObjectionDOW C700-35N Polypropylene Resin is intended for use in.. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Dow C7014-35RNA Polypropylene Impact Copolymer Resin DOW™ C7014-35RNA Polypropylene Resin is a high impact copolymer intended for injection molding processes. It is especially suited for thin-wall flow path molds.Main CharacteristicsFast set-upEasy .. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Dow H533-35RGU Polypropylene Homopolymer Resin OverviewExcellent spinnabilityConsistent processingAnti-gas-fadingUV resistantComplies with U.S. FDA 21 CFR 177.1520 (c)1.1aDOW H533-35RGU Polypropylene Resin is a controlled rheology grade intended.. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Dow H7012-35RN Polypropylene Homopolymer Resin OverviewGood processabilityGood mold fillingFaster cycle timesContains nucleating additiveComplies with U.S. FDA 21 CFR 177.1520 (c)1.1aDOW H7012-35RN Polypropylene Resin is intended for use in inje.. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Dow R792-35RNA Polypropylene Random Copolymer Resin OverviewControlled rheology productConsistent processabilityContains clarifying additiveContains an antistatic additiveComplies with U.S. FDA 21 CFR 177.1520 (c)3.1a, Canadian HPFB No ObjectionDOW R.. |
|||
Melt Index of Compound | 35 - 45 g/10 min @Load 2.16 kg, Temperature 190 °C |
35 - 45 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Arkema Group LOTRYL® 35 BA 40 Copolymer Ethylene - Butyl Acrylate LOTRYL® 35 BA 40 is a random copolymer of ethylene and butyl acrylate, prepared by the high pressure polymerization process. Co-monomer content is 35% in weight. LOTRYL® 35 BA 40 is particularly r.. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Arkema Group OREVAC® 18750 Maleic Anhydride Modified Polypropylene DescriptionOREVAC 18750 is a coextrusion coating adhesive based on a maleic anhydride modified polypropylene resin. It combines the processability of an extrusion coating resin with the thermal resi.. |
|||
Melt Index of Compound | 35 g/10 min @Temperature 230 °C |
35 g/10 min @Temperature 446 °F |
ASTM D1238 |
Amco PRIMATOP PP HOMO 350NA Injection Molding Polypropylene Features:nucleationanti-statlow viscosityexcellent processabilityexcellent stiffnessminimal odor or tasteApplications:thin wall partsclosuressmall appliancesFormer A-Top Polymers product; part of Am.. |
|||
Melt Index of Compound | 35 g/10 min | 35 g/10 min | ASTM D1238 |
Cheng Yu Plastic 3285 TPE Rubber |
|||
Melt Index of Compound | 35 - 45 g/10 min @Load 2.16 kg, Temperature 190 °C |
35 - 45 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Arkema Group EVATANE® 28-40 Copolymer Ethylene - Vinyl Acetate EVATANE® 28-40 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE® 28-40 is stabilized with antioxidants. The High Vinyl Acetate co.. |
|||
Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Amco PRIMATOP PP CO 350-40 Polypropylene Copolymer PP CO 350-40 features impact resistance and low temperature stiffness. Applications include injection molding and containers.Former A-Top Polymers product; part of Amco product line since 2013. |
|||
Melt Index of Compound | 35 g/10 min @Temperature 230 °C |
35 g/10 min @Temperature 446 °F |
ASTM D1238 |
Amco PRIMATOP PP CO 350-10 RC Clarified Random Copolymer Features:excellent processingimpactclarityanti-statApplications:rigid packaginghousewaresFormer A-Top Polymers product; part of Amco product line since 2013. |