Polymer Property : Melt Index of Compound = 20 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Index of Compound 15 - 20 g/10 min
15 - 20 g/10 min
I Preparation
Sibur ABS-TB (30,31) Molding Grade ABS Plastic
With high fluidity of melting, thermal and light resistance for large parts of devices, parts of refrigerators, and for hearing aids. Mark is allowed for contact with food products.
Melt Index of Compound 10 - 20 g/10 min

@Load 10.0 kg,
Temperature 345 °C
10 - 20 g/10 min

@Load 22.0 lb,
Temperature 653 °F
MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics LNP THERMOCOMP JF006 PES (Europe-Africa-Middle East)
LNP* Thermocomp* JF006 is a compound based on Polyethersulfone resin containing Glass Fiber.
Melt Index of Compound 15 - 20 g/10 min

@Load 2.16 kg,
Temperature 250 °C
15 - 20 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Shinkong Synthetic Fibers Shinite® D201K008 PBT, High Viscosity
Information from Shinkong Synthetic Fibers Corp.
Melt Index of Compound 15 - 20 g/10 min

@Load 2.16 kg,
Temperature 250 °C
15 - 20 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
Shinkong Synthetic Fibers Shinite® D201K008 PBT, High Viscosity
Information from Shinkong Synthetic Fibers Corp.
Melt Index of Compound 12 - 20 g/10 min
12 - 20 g/10 min
Sibur Discar-L PC/ABS Compositional Polymer
Composition material PC/ABS with high shock resistance, thermal, light, and atmospheric resistance for structural parts of technical purpose and parts for internal finishing of automobiles.
Melt Index of Compound 15 - 20 g/10 min
15 - 20 g/10 min
ASTM D1238
Cheng Yu Plastic PP228H TALC 10 Polypropylene, 10% Talc, High Heat
Melt Index of Compound 15 - 20 g/10 min
15 - 20 g/10 min
ASTM D1238
Cheng Yu Plastic PP229H TALC 20 Polypropylene, 20% Talc, High Heat
Melt Index of Compound 15 - 20 g/10 min
15 - 20 g/10 min
ASTM D1238
Cheng Yu Plastic PP230H TALC 30 Polypropylene, 30% Talc, High Heat
Melt Index of Compound 14 - 20 g/10 min

@Load 10.0 kg,
Temperature 220 °C
14 - 20 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238, ISO 1133
EPICHEM Epilac ABS Acrylonitrile Butadiene Styrene
Melt Index of Compound 15 - 20 g/10 min

@Load 10.0 kg,
Temperature 220 °C
15 - 20 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238, ISO 1133
EPICHEM Epilac ABS-BLACK Acrylonitrile Butadiene Styrene
Melt Index of Compound 15 - 20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
15 - 20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238, ISO 1133
EPICHEM Epilon FR-PC V0 Polycarbonate
Characteristics: self-extinguishing V0 at 1,6 mm
Melt Index of Compound 15 - 20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
15 - 20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238, ISO 1133
EPICHEM Epilon PC IX3000 Polycarbonate, High Impact
Characteristics: high fluidity, high impact
Melt Index of Compound 10 - 20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 - 20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238, ISO 1133
EPICHEM Epiryl B PPO Polyphenylene oxide
Melt Index of Compound 10 - 20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 - 20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238, ISO 1133
EPICHEM Epiryl PPO V0 Polyphenylene oxide
Characteristics: self-extinguishing V0 at 1,6 mm
Melt Index of Compound 15 - 20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
15 - 20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238, ISO 1133
EPICHEM Epicarb PC Polycarbonate
Characteristics: high fluidity, good impact
Melt Index of Compound 14 - 20 g/10 min

@Load 2.16 kg,
Temperature 190 °C
14 - 20 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Arkema Group EVATANE® 33-15 Copolymer Ethylene - Vinyl Acetate
EVATANE® 33-15 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE® 33-15 is stabilized with antioxidants. The High Vinyl Acetate co..