Polymer Property : Melt Index of Compound = 1.5 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Index of Compound	<= 1.5 g/10 min @Load 5.00 kg, Temperature 190 °C	<= 1.5 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
Polykemi AB POLYelast TPE Z706EX Thermoplastic Elastomer, SEBS-based Information provided by Polykemi AB
Melt Index of Compound	1.5 g/10 min	1.5 g/10 min	ASTM D1238
DuPont Elvax® 462 Ethylene-Vinyl Acetate Copolymer Resin (discontinued **) Elvax resins offer a unique combination of processing and performance characteristics. They provide outstanding toughness and resilience and maintain flexibility over a broad temperature range with..
Melt Index of Compound	1.5 g/10 min @Temperature 190 Â°C	1.5 g/10 min @Temperature 374 Â°F	ASTM D1238
Mitsui ADMERÂ® NF488A PE Type Polyolefin ADMERÂ® Adhesive Resin is a modified polyolefin with functional groups, designed to bond to a variety of polyolefins, ionomers, polyamides, ethylene vinyl alcohol (EVOH), polyesters (PET), polycar..
Melt Index of Compound	1.5 g/10 min	1.5 g/10 min	ASTM D1238
Lushan M-1 Adhesive Resin for Barrier Container and Tube Adhesive resin Lushan series for barrier container and tube is used for bonding a wide variety of materials, Itâ€™s most often used to adhering PE and EVOH, PP and EVOH, etc. Adhesive resins Lush..
Melt Index of Compound	1.5 - 2.4 g/10 min	1.5 - 2.4 g/10 min
Sibur 21020-PM1 Polypropylene with Low Haze For production of three-layer PE/PP film, for production of sheets for cups and thin casting. It is allowed for contact with food products.
Melt Index of Compound	1.5 g/10 min @Load 21.6 kg, Temperature 150 °C	1.5 g/10 min @Load 47.6 lb, Temperature 302 °F	Fainplast
Fainplast Compounds HAX HF 019/G Halogen Free PVC Sheathing; high flexibility
Melt Index of Compound	1.5 - 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	1.5 - 2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Arkema Group LOTRYL® 30 BA 02 Copolymer Ethylene - Butyl Acrylate LOTRYL® 30 BA 02 is a random copolymer of ethylene and butyl acrylate, prepared by the high pressure polymerization process. LOTRYL® 30 BA 02 is used for polymer modification, in compounds formula..
Melt Index of Compound	1.5 - 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	1.5 - 2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Arkema Group OREVAC® 9314 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre..