Polymer Property : Melt Index of Compound = 1.1 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Index of Compound	1.1 g/10 min @Load 3.80 kg, Temperature 230 Â°C	1.1 g/10 min @Load 8.38 lb, Temperature 446 Â°F	ASTM D1238
LG Chemical EH910 PMMA, General Purpose Grade for Extrusion Excellent solvent resistanceHighest of all grades in heat resistance, mechanical strength, surface hardness and stress cracking resistanceFeatures: Excellent transparency and eleganceWeather resista..
Melt Index of Compound	1.1 g/10 min @Load 10.0 kg, Temperature 190 Â°C	1.1 g/10 min @Load 22.0 lb, Temperature 374 Â°F	ASTM D1238
Sterigenics RaprexÂ® R-200 Branched High Density Polyethylene Applications: Injection Molding and ExtrusionRAPREXÂ® R-200 is a high density polyethylene based resin that exhibits an excellent balance of melt processability and physical properties due to its ..
Melt Index of Compound	1.1 g/10 min @Load 10.0 kg, Temperature 190 Â°C	1.1 g/10 min @Load 22.0 lb, Temperature 374 Â°F	ASTM D1238
Sterigenics RaprexÂ® R200D Branched High Density Polyethylene Applications: Injection Molding and ExtrusionRAPREXÂ® R200D is a high density polyethylene based resin that exhibits an excellent balance of melt processability and physical properties due to its ..
Melt Index of Compound	1.1 g/10 min @Load 2.16 kg, Temperature 190 °C	1.1 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Amco PRIMATOP HDPE RP 011 Granular High Density Polyethylene HDPE RP 011 features small particle size and is used in plastic lumber extrusion.Former A-Top Polymers product; part of Amco product line since 2013.
Melt Index of Compound	1.1 g/10 min @Temperature 230 °C	1.1 g/10 min @Temperature 446 °F	ASTM D1238
Amco PRIMATOP PP HOMO 011 Extrusion Processing Polypropylene PP HOMO 011 features high molecular weight, high isotactic, and does not contain slip or anti-block. Applications include strapping, various extrusion profile, and sheet and film applications.Former..