Polymer Property : Linear Mold Shrinkage, Transverse = 0.0063 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.0063 cm/cm	0.0063 in/in
Plastcom SLOVAMID 6 GF 30 FRA 3 PA6, 30% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 30% glass fibre, with halogen flame retardant. Main features: flammability in accordance with UL 94 V2 at 1.6 mm, glow wire at 850°C,..
Linear Mold Shrinkage, Transverse	0.0063 cm/cm	0.0063 in/in
Plastcom SLOVAMID 66 GB 30 GF 20 PA66, 20% glass fibre, 30% glass beads FeaturesPA 66 chemically reinforced with 20% glass fibre and with the content of 30 % glass beads. Improved anisotropy of shrinkage. The relation of the anisotropy to the mechanical properties can b..
Linear Mold Shrinkage, Transverse	0.0063 cm/cm	0.0063 in/in
Plastcom SLOVAMID 66 GF 25 FRA 5 PA66, 25% glass fibre, flame retardant FeaturesPA 66 for injection moulding, reinforced with 25% glass fibre and halogen flame retardant. Application in electrical industry: breakers, coilforms, covers, terminals. Slightly decreased flam..
Linear Mold Shrinkage, Transverse	0.0063 cm/cm	0.0063 in/in	60x60x2; 260Â°C / MT 80Â°C; 600 bar; ISO 294-4
Lanxess DurethanÂ® DP 1801/30 H3.0 000000 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, injection molding, halogen free flame retardant.Information provided by LANXESS.
Linear Mold Shrinkage, Transverse	0.0063 cm/cm	0.0063 in/in	ISO 294-4, 2577
Lanxess DurethanÂ® DP 1801/30 H3.0 000000 Nylon 6, 30% Milled Glass Fiber PA 6, injection molding grade, 30% milled fibers, UL 94V-2 at 0.8 mm, max. temperature in glow wire test: 960 Â°C at 0,75 mm, "halogen-free", good heat-ageing resistanceApplication Examples: Medic..
Linear Mold Shrinkage, Transverse	0.0063 - 0.0083 cm/cm @Time 86400 sec	0.0063 - 0.0083 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP GX07409H PSU LNP* LUBRICOMP* GX07409H is a compound based on PSU resin containing proprietary fillers. Added features of this grade include: Wear Resistant, Healthcare.
Linear Mold Shrinkage, Transverse	0.0063 - 0.0083 cm/cm @Time 86400 sec	0.0063 - 0.0083 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubricomp GX07409X PSU Wear resistant PSUThis data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse	0.0063 cm/cm	0.0063 in/in	SABIC Method
SABIC Innovative Plastics LNP THERMOCOMP NX07354 PC+ABS (Asia Pacific) This is a PC/ABS compound, a good candidate for Laser Direct Structuring applications.