Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Transverse | 0.000800 - 0.105 cm/cm | 0.000800 - 0.105 in/in | Average value: 0.00839 cm/cm Grade Count:221 |
Overview of materials for Polyphthalamide (PPA) This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide". Each property range of values reported is minimum and maximum values of appropriate Ma.. |
|||
Linear Mold Shrinkage, Transverse | 0.000800 - 0.00800 cm/cm | 0.000800 - 0.00800 in/in | Average value: 0.00415 cm/cm Grade Count:30 |
Overview of materials for Polycarbonate, Carbon Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Carbon Fiber Reinforced". Each property range of values reported is minimum and maximum v.. |
|||
Linear Mold Shrinkage, Transverse | 0.000800 - 0.00500 cm/cm | 0.000800 - 0.00500 in/in | Average value: 0.00373 cm/cm Grade Count:9 |
Overview of materials for Polycarbonate, Carbon + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Carbon + PTFE Filled". Each property range of values reported is minimum and maximum valu.. |
|||
Linear Mold Shrinkage, Transverse | 0.000800 - 0.0150 cm/cm | 0.000800 - 0.0150 in/in | Average value: 0.00824 cm/cm Grade Count:67 |
Overview of materials for Nylon 6, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |
|||
Linear Mold Shrinkage, Transverse | 0.000800 - 0.0170 cm/cm | 0.000800 - 0.0170 in/in | Average value: 0.00534 cm/cm Grade Count:241 |
Overview of materials for Polyetherimide (PEI) This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide". Each property range of values reported is minimum and maximum values of appropriate Mat.. |