Polymer Property : Linear Mold Shrinkage, Flow = 0.00500 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Flow 0.00500 - 0.00700 cm/cm

@Thickness 3.17 mm
0.00500 - 0.00700 in/in

@Thickness 0.125 in
ASTM D955
Oxford Polymers PC 714-FR Series PC, Flame retardant
Product Description: Amorphous, Polycarbonate injection molding grade, flame retardant Processing and Delivery Form: Pellets and Injection MoldingAdditives: Release Agents and UV stabilizersSpecial..
Linear Mold Shrinkage, Flow 0.00500 - 0.00700 cm/cm

@Thickness 3.17 mm
0.00500 - 0.00700 in/in

@Thickness 0.125 in
ASTM D955
Oxford Polymers PEI 1000 PEI
Product Description: (Unreinforced), Polyetherimide injection molding grade Processing and Delivery Form: Pellets and Injection Molding Special Characteristics: Colors AvailableInformation provided..
Linear Mold Shrinkage, Flow 0.00500 cm/cm

@Thickness 3.17 mm
0.00500 in/in

@Thickness 0.125 in
ASTM D955
Oxford Polymers PEI 10GF-Natural PEI, 10% Glass Fiber Reinforced
Product Description: Glass Fiber (10% Reinforced), Polyetherimide injection molding grade Processing and Delivery Form: Pellets and Injection Molding Additives: Release AgentsSpecial Characteristic..
Linear Mold Shrinkage, Flow 0.00500 - 0.00700 cm/cm
0.00500 - 0.00700 in/in
Injection and Compression; ISO 2577
Raschig Group EPOXIDUR® 3581 S ZC EP Epoxy Molding Compound
Inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Very good sealing connection on ..
Linear Mold Shrinkage, Flow 0.00500 - 0.00900 cm/cm
0.00500 - 0.00900 in/in
Injection and Compression; ISO 2577
Raschig Group MELOPAS® 156 MF Melamine
Glass fiber reinforced Melamine molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 200..
Linear Mold Shrinkage, Flow 0.00500 - 0.0100 cm/cm
0.00500 - 0.0100 in/in
Compression; ISO 2577
Raschig Group MELOPAS® 2010 MF Melamine
Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav..
Linear Mold Shrinkage, Flow 0.00500 - 0.00700 cm/cm

@Thickness 3.17 mm
0.00500 - 0.00700 in/in

@Thickness 0.125 in
ASTM D955
Oxford Polymers PC C20-000 Clear PC
Product Description: Amorphous, Unreinforced Polycarbonate injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Pigment onlySpecial Characteristics: Easy fl..
Linear Mold Shrinkage, Flow 0.00500 - 0.00700 cm/cm

@Thickness 3.17 mm
0.00500 - 0.00700 in/in

@Thickness 0.125 in
ASTM D955
Oxford Polymers PC/ABS 604i-FR PC/ABS, Flame retardant
Product Description: Amorphous, Polycarbonate & ABS, Flame retardant, Injection Molding Grade, VO rated @ 3.0mm. V2 rated @ 1.5mm Processing and Delivery Form: Pellets and Injection MoldingAdditive..
Linear Mold Shrinkage, Flow 0.00500 - 0.00700 cm/cm

@Thickness 3.17 mm
0.00500 - 0.00700 in/in

@Thickness 0.125 in
ASTM D955
Oxford Polymers PEI 1010 PEI
Product Description: (Unreinforced), Polyetherimide injection molding grade, high flow Processing and Delivery Form: Pellets and Injection Molding Additives: Release AgentsSpecial Characteristics: ..
Linear Mold Shrinkage, Flow 0.00500 - 0.00600 cm/cm
0.00500 - 0.00600 in/in
Compression; ISO 2577
Raschig Group 5567 DAP Diallyl Phthalate (DAP), Cast, Mineral Filler
Glass-fiber reinforced diallyl phthalate molding compound free from halogens. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exc..