Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Flow | 0.00400 cm/cm @Thickness 3.17 mm |
0.00400 in/in @Thickness 0.125 in |
ASTM D955 |
Oxford Polymers C-Acetal 25GF-BK Acetal, 25% Glass Fiber Reinforced Product Description: Glass Fiber (25% Reinforced), Acetal Injection Molding Grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Glass FiberSpecial Characteristics: Pre-color.. |
|||
Linear Mold Shrinkage, Flow | 0.00400 cm/cm @Thickness 3.17 mm |
0.00400 in/in @Thickness 0.125 in |
ASTM D955 |
Oxford Polymers C-Acetal -30GF-Natural Acetal Copolymer, 30% Glass Fiber Reinforced Product Description: Glass Fiber (30% Reinforced), Co-polymer Acetal, Injection Molding Grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Glass FiberSpecial Characteristic.. |
|||
Linear Mold Shrinkage, Flow | 0.00400 cm/cm @Thickness 3.17 mm |
0.00400 in/in @Thickness 0.125 in |
ASTM D955 |
Oxford Polymers PEI -20GF-Natural PEI, 20% Glass Fiber Reinforced Product Description: Glass Fiber (20% Reinforced), Polyetherimide injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Release Agents Special Characteristic.. |
|||
Linear Mold Shrinkage, Flow | 0.00400 - 0.00800 cm/cm | 0.00400 - 0.00800 in/in | Compression; ISO 2577 |
Raschig Group 4554 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to 300°C, exceptional electrical properties, good mechanical strength, very good dimensional stability. Processi.. |
|||
Linear Mold Shrinkage, Flow | 0.00400 - 0.00600 cm/cm | 0.00400 - 0.00600 in/in | Compression; ISO 2577 |
Raschig Group 6551 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
Linear Mold Shrinkage, Flow | 0.00400 - 0.00600 cm/cm | 0.00400 - 0.00600 in/in | Injection and Compression; ISO 2577 |
Raschig Group EPOXIDUR® 3581 T-1 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Very .. |
|||
Linear Mold Shrinkage, Flow | 0.00400 - 0.00700 cm/cm | 0.00400 - 0.00700 in/in | Compression; ISO 2577 |
Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
Linear Mold Shrinkage, Flow | 0.00400 - 0.00700 cm/cm | 0.00400 - 0.00700 in/in | Compression; ISO 2577 |
Raschig Group RALUPOL® 802 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up.. |
|||
Linear Mold Shrinkage, Flow | 0.00400 - 0.00700 cm/cm | 0.00400 - 0.00700 in/in | Compression; ISO 2577 |
Raschig Group RALUPOL® 804 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m.. |