Polymer Property : Linear Mold Shrinkage, Flow = 0.00400 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.00400 cm/cm @Thickness 3.17 mm	0.00400 in/in @Thickness 0.125 in	ASTM D955
Oxford Polymers C-Acetal 25GF-BK Acetal, 25% Glass Fiber Reinforced Product Description: Glass Fiber (25% Reinforced), Acetal Injection Molding Grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Glass FiberSpecial Characteristics: Pre-color..
Linear Mold Shrinkage, Flow	0.00400 cm/cm @Thickness 3.17 mm	0.00400 in/in @Thickness 0.125 in	ASTM D955
Oxford Polymers C-Acetal -30GF-Natural Acetal Copolymer, 30% Glass Fiber Reinforced Product Description: Glass Fiber (30% Reinforced), Co-polymer Acetal, Injection Molding Grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Glass FiberSpecial Characteristic..
Linear Mold Shrinkage, Flow	0.00400 cm/cm @Thickness 3.17 mm	0.00400 in/in @Thickness 0.125 in	ASTM D955
Oxford Polymers PEI -20GF-Natural PEI, 20% Glass Fiber Reinforced Product Description: Glass Fiber (20% Reinforced), Polyetherimide injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Release Agents Special Characteristic..
Linear Mold Shrinkage, Flow	0.00400 - 0.00800 cm/cm	0.00400 - 0.00800 in/in	Compression; ISO 2577
Raschig Group 4554 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to 300°C, exceptional electrical properties, good mechanical strength, very good dimensional stability. Processi..
Linear Mold Shrinkage, Flow	0.00400 - 0.00600 cm/cm	0.00400 - 0.00600 in/in	Compression; ISO 2577
Raschig Group 6551 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi..
Linear Mold Shrinkage, Flow	0.00400 - 0.00600 cm/cm	0.00400 - 0.00600 in/in	Injection and Compression; ISO 2577
Raschig Group EPOXIDUR® 3581 T-1 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Very ..
Linear Mold Shrinkage, Flow	0.00400 - 0.00700 cm/cm	0.00400 - 0.00700 in/in	Compression; ISO 2577
Raschig Group RALUPOL® 4802 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u..
Linear Mold Shrinkage, Flow	0.00400 - 0.00700 cm/cm	0.00400 - 0.00700 in/in	Compression; ISO 2577
Raschig Group RALUPOL® 802 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength, good heat resistance. This product meets the allowed up..
Linear Mold Shrinkage, Flow	0.00400 - 0.00700 cm/cm	0.00400 - 0.00700 in/in	Compression; ISO 2577
Raschig Group RALUPOL® 804 UP Polyester Glass-fiber reinforced polyester molding compound. Low molding shrinkage and post-shrinkage, good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy m..