Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | DIN 53 464 |
Perstorp Compounds Aminel GF Melamine Fiberglass-reinforced melamine material with high dimensional stability, excellent injection properties and high thermal stabilityInformation provided by Perstorp Compounds Inc. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm @Time 86400 sec |
0.0016 in/in @Time 24.0 hour |
ASTM D955 |
SABIC Innovative Plastics LNP KONDUIT OX10324 PPS (Asia Pacific) Thermally conductive mineral filled PPS FR compound, with through-plane and in-plane thermal conductivity of 3.5 W/(m*K) and 15 W/(m*K) respectively, conforming to ASTM E 1461 test standard. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | SABIC Method |
SABIC Innovative Plastics LNP LUBRICOMP DFL36E PC (Europe-Africa-Middle East) LNP* LUBRICOMP* DFL36E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features include; Internally Lubricated, Easy Molding. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | Injection molding; ISO 2577 |
Hexion Bakelite™ PF 1107 Phenolic Formaldehyde Resin, Low Shrinkage, Resistant to High Temperatures
(disconti Phenolic molding compound, inorganically filled, glass fiber reinforced, high heat resistance, low heat expansion coefficient, highest resistance to pressure, high dimensional stability.Application .. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | 150x105x3; 280°C / MT 80°C; 400 bar; ISO 2577 |
Lanxess Durethan® BKV 40 H2.0 901510 Nylon 6, Glass Fiber Reinforced PA 6, 40% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | 150x105x3; 280°C / MT 80°C; 400 bar; ISO 2577 |
Lanxess Durethan® BKV 50 000000 Nylon 6, Glass Fiber Reinforced PA 6, 50% glass fibers, injection moldingInformation provided by LANXESS. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm @Thickness 3.00 mm |
0.0016 in/in @Thickness 0.118 in |
Mold Temp 80°C; Melt Temp 280°C; 400 bar; ISO 294-4 |
Lanxess Durethan® BKV 50 H3.0 000000 Nylon 6, 50% Glass Fibers PA 6, 50% glass fibers, injection molding, heat-ageing stabilized |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | 150x105x3; 280°C / MT 80°C; 500 bar; ISO 2577 |
Lanxess Durethan® BKV 35 H3.0 000000 Nylon 6, Glass Fiber Reinforced PA 6, 35% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm @Thickness 3.17 mm |
0.0016 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES Elastoblend® PA6/6 GF14 IM HS L 14% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 14% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm @Thickness 3.17 mm |
0.0016 in/in @Thickness 0.125 in |
ASTM D955 |
Techmer ES Elastoblend® PA6/6 GF14 IM HS L BK 14% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 14% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | Eurotec |
Eurotec® Tecodur® PB70 NL TD20 PBT, unfilled, flame retardant - halogen (RoHS compliant), impact modified, natural Information provided by Eurotec® |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | ISO 294-4 |
Barlog Plastics KEBAFLOW HF130 LCP, 30% glass fiber reinforced LCP-GF30Information provided by BARLOG plastics GmbH. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | ISO 294-4 |
Barlog Plastics KEBAFLOW MF130 LCP, 30% glass fiber reinforced LCP-GF30Information provided by BARLOG plastics GmbH. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | ISO 294-4 |
Akro-Plastic Akromid® A3 GF 40 (1258) PA 6.6 Dry, 40% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat.. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | Sheet |
BASF Ultradur S 4090 G4 20% Glass Filled PBT Ultradur S 4090 G4 is a 20% glass reinforced PBT+ASA blend. It produces moldings with good surface finish,is resistant to chemicals and stress cracking, and has low shrinkage and warpage.Applicatio.. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | Sheet |
BASF Ultradur® S 4090 G6X 30% Glass Filled PBT Description: Is a PBT + ASA, low-warpage, free-flowing injection-molding grades with very good processing capabilities, containing 30% of glass fibers for industrial parts with high dimensional stab.. |
|||
Linear Mold Shrinkage, Flow | 0.0016 cm/cm | 0.0016 in/in | ISO 294-4, 2577 |
Lanxess Pocan® B 700 000000 PBT
(discontinued **) PBT, non-reinforced, extrusion, improved flowability |