Polymer Property : Linear Mold Shrinkage, Transverse = 0.021 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly LNP* Thermocomp* KF003 is a compound based on Acetal Copolymer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly (Asia Pacific) LNP* Thermocomp* KF003 is a compound based on Acetal Copolymer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Linear Mold Shrinkage, Transverse	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RB008 PA 66 (Asia Pacific) LNP THERMOCOMP* RB008 is a compound based on Nylon 66 resin containing Glass Bead.
Linear Mold Shrinkage, Transverse	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP RB008 PA 66 (Asia Pacific) LNP THERMOCOMP* RB008 is a compound based on Nylon 66 resin containing Glass Bead.
Linear Mold Shrinkage, Transverse	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RB008 PA 66 LNP THERMOCOMP* RB008 is a compound based on Nylon 66 resin containing 40% Glass Bead.
Linear Mold Shrinkage, Transverse	0.019 - 0.021 cm/cm @Time 86400 sec	0.019 - 0.021 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP RB008 PA 66 LNP THERMOCOMP* RB008 is a compound based on Nylon 66 resin containing 40% Glass Bead.
Linear Mold Shrinkage, Transverse	0.018 - 0.021 cm/cm @Thickness 4.00 mm	0.018 - 0.021 in/in @Thickness 0.157 in	Normal, 24h; ISO 294-4
DuPont Performance Polymers Delrin® 111P NC010 Acetal Homopolymer Delrin® 111P is a high viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, fewer voids). It has higher tensile strength and mod..