Polymer Property : Linear Mold Shrinkage, Transverse = 0.017 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Transverse 0.015 - 0.017 cm/cm

@Time 86400 sec
0.015 - 0.017 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP COLORCOMP M1000S PP
LNP COLORCOMP* M1000S is an unfilled Polypropylene resin. Added features of this material include: Heat Stabilized.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 195 PBT
PELLET FORM. For compounding only (not for injection molding). Unreinforced PBT. Melt viscosity between 740 and 900 poise. Natural Color (1001) Only.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 195HP PBT
PELLET FORM. For compounding only (not for injection molding). Unreinforced PBT. FDA 21CFR177.1660 compliant. Melt viscosity between 740 and 900 poise. Natural Color (1001) Only.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 215HPR PBT
Unreinforced PBT with mold release. FDA food contact compliant in limited colors. Effective March 2008 this grade will no longer be supported with biocompatibility data. Alternative grade Valox HX21..
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 295 PBT
Unreinforced PBTThis data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 310 PBT
Unreinforced, general purpose. Typical viscosity 5000-7000.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 310 PBT (Asia Pacific)
Unreinforced, general purpose. Typical viscosity 5000-7000.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 310HP PBT
PBT for compounding/fibers only. Not intended for injection molding. FDA compliant. Available in Natural color (1001) only.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 311 PBT
Unreinforced, improved resistance to UV. Medium viscosity.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 312 PBT
Unreinforced, For compounding only (not for injection molding), FDA (21 CFR 177.1660) compliant. Medium viscosity.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 312 PBT (Asia Pacific)
Unreinforced, For compounding only (not for injection molding), Medium viscosity.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 315 PBT
Unreinforced, For extrusion/compounding only (not for injection molding). High viscosity. Melt viscosity between 7500 and 9500 poise.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 325 PBT
General purpose, unreinforced, improved processing. Applications like sprinklers and nozzles, pumps, door handle, tank covers, pens, pencils etc.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 325 PBT (Asia Pacific)
General purpose, unreinforced, improved processing. Applications like sprinklers and nozzles, pumps, door handle, tank covers, pens, pencils etc.
Linear Mold Shrinkage, Transverse 0.010 - 0.017 cm/cm

@Thickness 0.750 - 2.30 mm
0.010 - 0.017 in/in

@Thickness 0.0295 - 0.0906 in
SABIC Method
SABIC Innovative Plastics Valox® 325M PBT (Asia Pacific)
325M is a high flow VALOX 325 for restrictive gate tooling (key buttons)This data was supplied by SABIC-IP for the Asia Pacific region.
Linear Mold Shrinkage, Transverse 0.015 - 0.017 cm/cm

@Time 86400 sec
0.015 - 0.017 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly
LNP* THERMOCOMP* KF002L is a compound based on Acetal Homopolymer resin containing 10% Glass Fiber. Added features of this material include: Low Extractible.
Linear Mold Shrinkage, Transverse 0.015 - 0.017 cm/cm

@Time 86400 sec
0.015 - 0.017 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly (Asia Pacific)
LNP* Thermocomp* KF002L is a compound based on Acetal Homopolymer resin containing Glass Fiber. Added features of this material include: Low Extractible.
Linear Mold Shrinkage, Transverse 0.015 - 0.017 cm/cm

@Time 86400 sec
0.015 - 0.017 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT
LNP* THERMOCOMP* WFB54 is a compound based on PBT resin containing 20% Glass Fiber, 25% Glass Bead.
Linear Mold Shrinkage, Transverse 0.015 - 0.017 cm/cm

@Time 86400 sec
0.015 - 0.017 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT (Asia Pacific)
LNP* Thermocomp* WFB54 is a compound based on Polybutylene Terephalate resin containing Glass Bead.
Linear Mold Shrinkage, Transverse 0.0157 - 0.017 cm/cm

@Time 86400 sec
0.0157 - 0.017 in/in

@Time 24.0 hour
ASTM D 955
SABIC Innovative Plastics LNP Lubricomp KFI12A Acetal Homopolymer
LNP LUBRICOMP* KFI12A is a compound based on Acetal Homopolymer resin containing Glass Fiber, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABI..