Polymer Property : Linear Mold Shrinkage, Transverse = 0.015 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage, Transverse 0.015 - 0.017 cm/cm

@Time 86400 sec
0.015 - 0.017 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP COLORCOMP M1000S PP
LNP COLORCOMP* M1000S is an unfilled Polypropylene resin. Added features of this material include: Heat Stabilized.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP KONDUIT ITF2B PA 6/12 (Asia Pacific)
LNP* Konduit* ITF2B is a compound based on Nylon 6/12 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66 (Europe-Africa-Middle East)
LNP* Konduit* RTF2B is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66
LNP* KONDUIT* RTF2B is a compound based on Nylon 66 resin containing 10% Glass Fiber, 55% Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66 (Asia Pacific)
LNP* Konduit* RTF2B is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly (Asia Pacific)
LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data ..
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP RX05495 PA 66
LNP LUBRICOMP* RX05495 is a compound based on Nylon 66 resin containing Glass Bead, Graphite, Glass Fiber. Added features of this material include: Easy Molding.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP RX05495 PA 66
LNP LUBRICOMP* RX05495 is a compound based on Nylon 66 resin containing Glass Bead, Graphite, Glass Fiber. Added features of this material include: Easy Molding.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT
LNP* Lubricomp* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Ret..
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT (Asia Pacific)
LNP* Lubricomp* WFL369 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Ret..
Linear Mold Shrinkage, Transverse 0.015 - 0.035 cm/cm

@Time 86400 sec
0.015 - 0.035 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP STAT-KON KX02764 Acetal
LNP STAT-KON* KX02764 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
Linear Mold Shrinkage, Transverse 0.015 - 0.035 cm/cm

@Time 86400 sec
0.015 - 0.035 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP STAT-KON KX02764 Acetal
LNP STAT-KON* KX02764 is a compound based on Acetal resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP STAT-KON RFD02 PA 66
LNP* STAT-KON* RFD02 is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP STAT-KON RFD02 PA 66 (Asia Pacific)
LNP* Stat-kon* RFD02 is a compound based on Nylon 66 resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP HB006 PA 11 (Asia Pacific)
LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing Glass Bead.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP THERMOCOMP HB006 PA 11 (Asia Pacific)
LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing Glass Bead.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP HB006 PA11
LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing 30% Glass Bead.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP THERMOCOMP HB006 PA11
LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing 30% Glass Bead.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12
LNP* Thermocomp* IFB33 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP Thermocomp IFB33 PA 6/12 (Asia Pacific)
LNP* Thermocomp* IFB33 is a compound based on Nylon 6/12 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Linear Mold Shrinkage, Transverse 0.015 - 0.017 cm/cm

@Time 86400 sec
0.015 - 0.017 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly
LNP* THERMOCOMP* KF002L is a compound based on Acetal Homopolymer resin containing 10% Glass Fiber. Added features of this material include: Low Extractible.
Linear Mold Shrinkage, Transverse 0.015 - 0.017 cm/cm

@Time 86400 sec
0.015 - 0.017 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly (Asia Pacific)
LNP* Thermocomp* KF002L is a compound based on Acetal Homopolymer resin containing Glass Fiber. Added features of this material include: Low Extractible.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP THERMOCOMP MH0500C PP (Asia Pacific)
LNP* Thermocomp* MH0500C is a compound based on Polypropylene resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Linear Mold Shrinkage, Transverse 0.015 - 0.017 cm/cm

@Time 86400 sec
0.015 - 0.017 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT
LNP* THERMOCOMP* WFB54 is a compound based on PBT resin containing 20% Glass Fiber, 25% Glass Bead.
Linear Mold Shrinkage, Transverse 0.015 - 0.017 cm/cm

@Time 86400 sec
0.015 - 0.017 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT (Asia Pacific)
LNP* Thermocomp* WFB54 is a compound based on Polybutylene Terephalate resin containing Glass Bead.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP WX05456 Polyester, TP
LNP THERMOCOMP* WX05456 is a compound based on Polyester, TP resin containing Mineral.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly
LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data ..
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
0.015 in/in

@Time 24.0 hour
ISO 294
SABIC Innovative Plastics LNP THERMOCOMP MH0500C PP
LNP* THERMOCOMP* MH0500C is a compound based on Polypropylene resin. Added feature of this material is: High Specific Gravity.
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Temperature 240 °C
0.015 in/in

@Temperature 464 °F
ASTM D3392
DuPont™ Nomex® Type 993, 160 mil Nominal Thickness Medium-Density Aromatic Nylon Pressboard
Type 993 is a medium-density pressboard which offers a balance of rigidity and conformability along with outstanding saturability and excellent properties in air and oil. Typical applications includ..