Polymer Property : Density = 0.284 lb/in³ Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Density 7.86 g/cc
0.284 lb/in³
Latrobe CBS-50â„¢ NiL VIM-VAR High Performance Carburizing Bearing and Gear Steel
CBS-50 NiL VIM-VAR is a carburizing bearing and gear steel designed for service temperatures up to 600°F. The chemistry is engineered such that when suitably carburized and heat treated the case ..
Density 7.87 g/cc
0.284 lb/in³
Estimated by MatWeb
SSAB Tunnplat Aluzink 220A RP-X High-strength Metal-coated Steel
High-strength Metal-coated SteelComments: Aluzink RP - rephosphorized steel (aluminum-zinc coated sheet). Property values are for thicknesses 0.5 - 1.5 mm. Iron content is approximate - exact compo..
Density 7.87 g/cc
0.284 lb/in³
Estimated by MatWeb
SSAB Tunnplat Aluzink B500A Metal-coated Mild Steel
Metal-coated Mild SteelComments: Aluzink - Aluminum-zinc coated sheet. Property values are for thicknesses 0.4 - 2.00 mm. Iron content is approximate - exact composition is not reported by the manu..
Density 7.87 g/cc
0.284 lb/in³
Estimated by MatWeb
SSAB Tunnplat Docol® 1000 DP High-strength Steel
High-strength SteelCharacteristics: The steels are annealed at temperatures between 750°C and 850°C, depending on the grade of steel, and then are hardened by quenching in water. Tempering is..
Density 7.87 g/cc
0.284 lb/in³
Estimated by MatWeb
SSAB Tunnplat Docol® 500DP High-strength Steel
High-strength SteelComments: Docol DP - Cold Rolled Steel - dual-phase steel. Property values are for cold-rolled steel; thicknesses 0.5 - 1.6 mm. Iron content is approximate - exact composition is..
Density 7.87 g/cc
0.284 lb/in³
Estimated by MatWeb
SSAB Tunnplat Docol® DC04 (Fe P04) Deep-drawing Steel
Deep-drawing SteelComments: Docol - Cold Rolled Mild Steel. Property values are for cold-rolled steel; thicknesses 0.40 - 3.00 mm. Iron content is approximate - exact composition is not reported b..
Density 7.87 g/cc
0.284 lb/in³
Estimated by MatWeb
SSAB Tunnplat Dogal 280YP High-strength Metal-coated Steel
High-strength Metal-coated SteelComments: Dogal YP - HSLA steel. Property values are for thicknesses 0.4 to 2.5 mm. Iron content is approximate - exact composition is not reported by the manufactur..
Density 7.87 g/cc
0.284 lb/in³
Estimated by MatWeb
SSAB Tunnplat Dogal B420 Metal-coated Mild Steel
Metal-coated Mild SteelComments: Dogal - Hotdipped-galvanized sheet. Property values are for thicknesses 0.5 - 2.5 mm. Iron content is approximate - exact composition is not reported by the manufac..
Density 7.87 g/cc
0.284 lb/in³
Estimated by MatWeb
SSAB Tunnplat Dogal F26 Metal-coated Mild Steel
Metal-coated Mild SteelComments: Dogal - Hotdipped-galvanized sheet. Property values are for thicknesses 0.5 - 2.5 mm. Iron content is approximate - exact composition is not reported by the manufac..
Density 7.87 g/cc
0.284 lb/in³
Estimated by MatWeb
SSAB Tunnplat Domex® 024 BOR Oil quenched Boron Steel
Domex® is the brand name of hot rolled products from SSAB Tunnplat. Compared to conventional quenched and tempered steels, boron steel have several benefits including better formability. Boron ..
Density 7.87 g/cc
0.284 lb/in³
Estimated by MatWeb
SSAB Tunnplat Domex® 034 BOR Water quenched Boron Steel
Domex® is the brand name of hot rolled products from SSAB Tunnplat. Compared to conventional quenched and tempered steels, boron steel have several benefits including better formability. Boron ..
Density 7.85 g/cc
0.284 lb/in³
Williams Advanced Alloys WS199 Solder
All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys
Density 7.86 g/cc
0.284 lb/in³
Wingate Alloys Winco NT 24 Nitrogen-Strengthened Austenitic Stainless Steel
Winco NT 24 provides good aqueous corrosion resistance combined with resistance to abrasives, metal-to-metal wear and sustained heats of 1500°F. Higher mechanical properties than standard austeniti..
Density 7.85 g/cc
0.284 lb/in³
ThyssenKrupp XABO® 500 Structural Steel
This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-..
Density 7.87 g/cc

@Temperature 20.0 °C
0.284 lb/in³

@Temperature 68.0 °F
AK Steel ASTM A 1011, Grade 55 Hot Rolled Carbon Steel, Structural Steel (SS)
Information provided by AK Steel
Density 7.87 g/cc
0.284 lb/in³
AK Steel ASTM A 715 Class 2 Formable, Grade 50F Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA)
ASTM A 715 is for Hot Rolled and Cold Rolled grades. AK Steel produces Type 1 (columbium bearing only), Class 2 limits only C and has a 10 ksi difference between the minimum specified YS and UTS. ..
Density 7.87 g/cc
0.284 lb/in³
AK Steel ASTM A 907, Grade 30 Hot Rolled Carbon Steel, Structural Quality (SQ)
For gauges up to 0.229", ASTM A 570 must be specified, gauges >0.230", ASTM A 907 must be used. Items 0.180 to 0.230" gauge which are >48" wide may be ordered to either A 570 or A 907.Information p..
Density 7.87 g/cc
0.284 lb/in³
AK Steel Cold Rolled Carbon Steel, Bake Hardenable (BH 210), SAE J2340 Type 210 B
Information provided by AK Steel
Density 7.87 g/cc
0.284 lb/in³
AK Steel Cold Rolled Carbon Steel, Dent Resistant (DR 210), SAE J2340 Type 210 A
Information provided by AK Steel
Density 7.87 g/cc
0.284 lb/in³
AK Steel ZINCGRIP® ELECTRASMOOTH® Electrogalvanized Carbon Steel, Bake Hardenable (BH 250)
Brake Hardenable steels offer good formability and an increase in strength after paint bake.Information provided by AK Steel
Density 7.87 g/cc
0.284 lb/in³
AK Steel ZINCGRIP® ELECTRASMOOTH® Electrogalvanized Carbon Steel, Dent Resistant (DR 210)
Compared to DS Type B, DR steels have higher initial YS which contributes to increased strength after forming.Information provided by AK Steel
Density 7.86 g/cc
0.284 lb/in³
ATI Allegheny Ludlum AL 304DA Stainless/Carbon Steel Three-Ply Composite
Composition above represents only the Type 304 cladding. Its iron content calculated as balance.Allegheny Ludlum AL 304DA is tri-ply composite consisting of a dual stabilized, low carbon steel cent..
Density 7.85 g/cc

@Temperature 23.0 °C
0.284 lb/in³

@Temperature 73.4 °F
Carpenter Gall-Tough® Stainless
Data provided by Carpenter Technology Corporation.6.4 mm diameter tensile specimens from center of 25.4 mm diameter bar annealed 1066°C 1 hour, water quenched, and ground.Threshold Galling Stress 1..
Density 7.87 g/cc
0.284 lb/in³
AK Steel ASTM A 570, Grade 45 Hot Rolled Carbon Steel, Structural Quality (SQ)
For gauges up to 0.229", ASTM A 570 must be specified, gauges >0.230", ASTM A 907 must be used. Items 0.180 to 0.230" gauge which are >48" wide may be ordered to either A 570 or A 907.Information p..
Density 7.87 g/cc
0.284 lb/in³
AK Steel ZINCGRIP® 230, Grade 33 Hot Dip Galvanized Carbon Steel, Structural Steel (SS)
Information provided by AK Steel
Density 7.87 g/cc
0.284 lb/in³
AK Steel ZINCGRIP® ELECTRASMOOTH® Electrogalvanized Carbon Steel, Extra Deep Drawing Steel Plus (EDDS+), Standard Grade
Interstitial Free (I-F) steels are made by adding titanium to the molten steel after degassing and offer excellent drawability.Information provided by AK Steel
Density 7.87 g/cc
0.284 lb/in³
AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, Bake Hardenable (BH 210)
Information provided by AK Steel
Density 7.87 g/cc
0.284 lb/in³
AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, Dent Resistant (DR 180)
Information provided by AK Steel
Density 7.85 g/cc

@Temperature 23.0 °C
0.284 lb/in³

@Temperature 73.4 °F
Carpenter Gall-Tough® Stainless, Annealed and Cold Drawn Bar, 10% Cold Work
Data provided by Carpenter Technology Corporation.Threshold Galling Stress 103 MPa (higher stress tests not performed). The avg. total volume loss on the wear test is 5 mm³ at 100 rpm.Gall-Tough®..