Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 2.10 - 2.20 g/cc | 0.0759 - 0.0795 lb/in³ | ASTM D792 |
Polikim EFALON® T-100 Virgin PTFE Applications: Gaskets, seals, O-rings, V-Rings, compression packings and similar sealing parts, Bushes, bearings and piston rings, Electrical insulators, Sliding supports, Conveyor belts, Coated tu.. |
|||
Density | 2.16 - 2.20 g/cc | 0.0780 - 0.0795 lb/in³ | ASTM D792-50 |
Mikro-Technik Reproflon PTFE Reproflon is reclaimed PTFE scraps. The powder can be reused for the usual manufacturing procedures.Information provided by Mikro-Technik GmbH |
|||
Density | 2.16 - 2.20 g/cc | 0.0780 - 0.0795 lb/in³ | |
Mikro-Technik Reproflon G25 PTFE Available Forms: Rods, Tubes. Special Characteristics:Higher resistance to abrasionHigher resistance to compression compared to virgin PTFE and unfilled ReproflonReduced plastic flowInformation prov.. |
|||
Density | 1.20 - 2.20 g/cc @Pressure 0.101 MPa, Temperature 20.0 °C |
0.0434 - 0.0795 lb/in³ @Pressure 14.7 psi, Temperature 68.0 °F |
|
BASF Palusol® 100 Silicate Panel Relevant identified uses: Intumescent plates for use as fire protection in the building industryInformation provided by BASF |
|||
Density | 1.20 - 2.20 g/cc @Pressure 0.101 MPa, Temperature 20.0 °C |
0.0434 - 0.0795 lb/in³ @Pressure 14.7 psi, Temperature 68.0 °F |
|
BASF Palusol® 104 Silicate Panel Relevant identified uses: Intumescent plates for use as fire protection in the building industryInformation provided by BASF |
|||
Density | 1.90 - 2.20 g/cc | 0.0686 - 0.0795 lb/in³ | |
Aremco Ceramabond™ 552 High Temperature Ceramic Adhesive/Paste, Alumina Filled Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and.. |
|||
Density | 1.90 - 2.20 g/cc | 0.0686 - 0.0795 lb/in³ | |
Aremco Ceramabond™ 571 High Temperature Ceramic Adhesive/Paste, Magnesium Oxide Filled Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and.. |
|||
Density | 1.20 - 2.20 g/cc @Pressure 0.101 MPa, Temperature 20.0 °C |
0.0434 - 0.0795 lb/in³ @Pressure 14.7 psi, Temperature 68.0 °F |
|
BASF Palusol® 210 Silicate Panel Relevant identified uses: Intumescent plates for use as fire protection in the building industryInformation provided by BASF |
|||
Density | 2.00 - 2.20 g/cc | 0.0723 - 0.0795 lb/in³ | Molded |
Bulk Molding Compounds BMC T12-15541 General Purpose Molding Compound BMC T12 is a general purpose molding compound. Due to the excellent flow and controlled reactivity, BMC T12 is well suited for injection, transfer or compression molding of intricate parts. Typica.. |
|||
Density | 2.13 - 2.20 g/cc | 0.0770 - 0.0795 lb/in³ | ASTM D792 |
Guarniflon PTFE G200 Polytetrafluoroethylene A virgin PTFE with low coefficient of friction, excellent chemical inertness, non-adhesive surface, wide service temperature range, and excellent dielectric propertiesInformation provided by Guarnif.. |
|||
Density | 2.10 - 2.20 g/cc | 0.0759 - 0.0795 lb/in³ | apparent |
Beijing Evergrow Resources PTFE Extrusion Tube Features:PTFE extruded tubing is manufactured by high pressure PTFE dispense resin mixed with additive, it is extruded and sintered. According to different demands, the tubing could be opaque or tra.. |
|||
Density | 1.00 - 2.20 g/cc | 0.0361 - 0.0795 lb/in³ | Average value: 1.76 g/cc Grade Count:71 |
Overview of materials for Epoxy, Molded, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Molded, Glass Fiber Filler". Each property range of values reported is minimum and maximum values.. |
|||
Density | 2.13 - 2.20 g/cc | 0.0770 - 0.0795 lb/in³ | ASTM D792 |
Guarniflon PTFE G300 Polytetrafluoroethylene A virgin PTFE with low coefficient of friction, excellent chemical inertness, non-adhesive surface, wide service temperature range, and excellent dielectric propertiesInformation provided by Guarnif.. |